Abstract
In the article, the influence of low-temperature nitrocarburizing on the structure and properties of Х12Ф1 steel was considered. It was found that for Х12Ф1 steel the highest values of micro-hardness are achieved at a saturation temperature of 550 °С and amount to 12,000 MPa at a four-hour saturation.