%0 Generic %1 jeroense1997interface %A Jeroense, M %A Lindgren, M %A Gustafsson, A %A Schutte, T %D 1997 %K POLYMER-LAMINATES %T INTERFACE CHARGE IN POLYMER LAMINATES %X Dielectric sample combinations were tested in a Pulse Electro Acoustic measurement set-up. It was seen that charge accumulates in a predictable way due to a difference in resistivity and permittivity of the materials. Furthermore it was seen that flame-oxidation of the surface of a specific material diminishes the charge accumulation at the insulator/insulator interface. No relation could be found between different grades of surface roughness and charge accumulation at the interface.

@conference{jeroense1997interface, abstract = {Dielectric sample combinations were tested in a Pulse Electro Acoustic measurement set-up. It was seen that charge accumulates in a predictable way due to a difference in resistivity and permittivity of the materials. Furthermore it was seen that flame-oxidation of the surface of a specific material diminishes the charge accumulation at the insulator/insulator interface. No relation could be found between different grades of surface roughness and charge accumulation at the interface.}, added-at = {2020-04-03T16:01:41.000+0200}, author = {Jeroense, M and Lindgren, M and Gustafsson, A and Schutte, T}, biburl = {https://www.bibsonomy.org/bibtex/2717410fabdabf9b68eb0cad874d40080/ceps}, eventdate = {June 22-25}, eventtitle = {IEEE International Conference on Conduction and Breakdown in Solid Dielectrics}, interhash = {dae176fb61148233852c7b90ca527a5e}, intrahash = {717410fabdabf9b68eb0cad874d40080}, keywords = {POLYMER-LAMINATES}, timestamp = {2023-12-20T14:38:22.000+0100}, title = {INTERFACE CHARGE IN POLYMER LAMINATES}, venue = {Sweden}, year = 1997 }